Mechanism Analysis of High Temperature Decay of NCM622 Material
专栏:Industry Information
发布日期:2018-06-08
阅读量:1907
作者:admin
收藏:
The following figure shows the EIS analysis results of NCM622 materials under different cut-off voltages and different cycle times.


Lithium Grid
 News: With the continuous improvement of the specific energy of lithium-ion batteries , the specific capacity requirements of the positive and negative materials are getting higher and higher. The traditional LiCoO2 material has a capacity of only about 140 mAh/g, which cannot meet the requirements of the new generation of high energy density batteries . Demand, and the increasingly crazy cobalt price became the last straw to crush LCO. Therefore, people turned their attention to NCM materials with higher capacity and more favorable price. Compared with LCO materials, the specific capacity of NCM materials has been greatly improved (the capacity of NCM622 materials can reach 170-180mAh/g), and because The use of Co is greatly reduced, so NCM has a clear advantage over LCO materials in terms of price, which makes NCM the new favorite of lithium-ion battery . However, there is still a serious problem in NCM materials - high temperature cycle performance is not good, and the NCM material capacity degradation is greatly accelerated at high temperatures, which seriously affects the service life of lithium ion batteries.

Recently, Siyang Liu et al. of Fudan University in Shanghai conducted in-depth research on the mechanism of high temperature cycling of NCM622 materials at 55 °C. Studies have shown that NCM622 materials in the process of high temperature and high voltage cycle, the metal cations in the surface will be severely mixed, resulting in a significant increase in charge exchange resistance. In addition, high temperature and high voltage cycling will increase the decomposition of LiPF6 on the electrode surface, increase the content of LiF and NiF2, and increase the electrode/ electrolyte interface impedance.

1564016989174019559.jpg

1564017021011017112.jpg

Siyang Liu first synthesized the NCM622 material by solid phase method. The XRD pattern showed that the synthesized NCM622 material had a well-developed layered a-NaFeO2 structure. Figure a below shows the first charge-discharge curve of Siyang Liu synthesized NCM622 material under different cut-off voltages. It can be seen from the figure that as the cut-off voltage is gradually increased to 4.3V, 4.5V and 4.7V, the material capacity is reached. 176, 201.3 and 218.1 mAh/g, although higher cut-off voltages can lead to higher capacity, but also cause a very rapid decline in the cycle performance of NCM622 materials. It can be seen from the following figure b that when the cutoff voltage is 4.3V, 4.5V and 4.7V, respectively, the capacity retention rate of the NCM622 material cycled at 55 °C for 50 times is 96.3%, 90.7% and 78.9%, respectively. The voltage has an important influence on the cycle performance of the NCM622 material.

1564016990271006909.jpg

The study of the decay mechanism of NCM622 materials at different cut-off voltages found that a higher cut-off voltage significantly increased the interfacial resistance of the NCM622 material. The following figure shows the EIS analysis results of NCM622 materials under different cut-off voltages and different cycle times. It can be seen that all the curves are composed of two arcs and a straight line, which indicates that there are two interfaces on the surface of the material: The surface of the NCM622 material is decomposed to form an interfacial film. Siyang Liu fits the EIS results using the equivalent circuit in Figure c below. Siyang Liu considers Rs1 as the impedance of the interface film and Rct as the charge exchange impedance. When the cutoff voltage is 4.3V, 4.5V and 4.7V, respectively, the Rs1 of the material is 17, 20 and 21.6W, respectively, and after 25 cycles, Rs1 is increased to 18.7, 23.4 and 28.2W, respectively, indicating a higher cutoff. The voltage causes the growth and reconstruction of the interfacial film of the NCM622 material, thereby increasing the interfacial resistance.

During the cyclic process, the charge exchange resistance Rct changes more significantly. It can be seen from the figure that the Rct of the NCM622 material is only slightly increased 25 times when the cutoff voltage is 4.3V, but the cycle is 25 times after the cutoff voltage is 4.5V and 4.7V. The Rct of the material was increased by 2 times and 8 times, respectively. This may be because a higher cut-off voltage causes the NCM 622 material to dislodge more Li, thus resulting in an increase in the Li/Ni misculation of the material and an irreversible phase change of the material, resulting in an increase in the charge exchange resistance of the material.

 

1564017021718048760.jpg

EIS analysis shows that the increase of the interface impedance of the material is closely related to the decline of the capacity of the material, but the mechanism of action is still unclear. The figure below shows the SEM picture of the new electrode and the electrode after cycling at different voltages. We can see that there is a significant increase in the number of cracks on the surface of the electrode after cycling, especially at the electrode surface after cycling at a higher cut-off voltage. The cracks become more serious. These cracks on the surface of the electrode may cause some of the active material to lose its connection with the Al foil and the conductive network, resulting in loss of the active material, resulting in partial capacity degradation.

1564016990377082067.jpg

Generally, we believe that the side reaction mainly occurs at the electrode/electrolyte interface, so the electrode/electrolyte interface is more susceptible to erosion. Therefore, Siyang Liu used HRTEM to detect the surface layer of NCM622 after cycling at different voltages. Through high-resolution TEM images, we noticed that the new NCM622 has a well-developed crystal structure. After circulating 50 times at a cutoff voltage of 4.3V, the body of the NCM622 material still maintains a well-developed layered structure, but on the surface of the material. It can be observed that transition metal ions are mixed in some areas. When the cut-off voltage is increased to 4.5V and 4.7V, the crystal structure of the material decays more severely. It can be seen from the figure that excessive Li removal at high cut-off voltage causes metal cations to enter the Li layer, which blocks The diffusion channel of Li reduces the active site of Li, resulting in an increase in interface charge exchange impedance and a decrease in reversible capacity, which is consistent with previous EIS analysis results.

It is also worth noting that at higher cut-off voltages, some holes can be observed on the surface of the material after cycling, mainly due to the release of O and the dissolution of the transition metal in the material at higher cut-off voltages.

1564017021566000388.jpg

In view of the mechanism of the increase of the electrode/electrolyte interface resistance Rs1, Siyang Liu analyzed the surface of the NCM622 material by XPS and found that the electrolyte decomposition product showed a significant increase after the cycle. In particular, the LiF content of the electrode surface after LiF circulated at a cutoff voltage of 4.3V was 8.9%, but the LiF content of the electrode surface increased to 14.9% and 17% when the cutoff voltage was increased to 4.5V and 4.7V, while passing XPS. Analysis also found that the surface of the electrode showed a significant increase in the content of NiF2 after the cycle, which indicates that the decomposition process of the electrolyte on the surface of the NCM622 material is accompanied by the dissolution of the transition metal element. Siyang Liu believes that this is mainly due to the HF pair produced by the decomposition of LiPF6. The NCM622 material is corroded, causing the dissolution of transition metal elements.

7.jpg

The work of Siyang Liu shows that the circulation of NCM622 material at high temperature and high cut-off voltage will cause the increase of the transition metal element and Li in the material of the electrode surface, causing the decay of the surface crystal structure of NCM622 material, resulting in an increase in charge exchange resistance and The reversible capacity is reduced. Cycling at high temperature and high voltage also causes decomposition of LiPF6 on the electrolysis surface, resulting in an increase in the content of LiF and NiF2 on the surface of the NCM622 material, resulting in an increase in the electrode/electrolyte interface impedance of the NCM622 material.

8.jpg

上一页:Industrial chain demand, fuel cell commercialization is full of opportunities
下一页:Inventory: Top 10 materials that have the greatest potential for improving lithium battery performan